Formation analysis of edge cracks of 33MnCrTiB fork steel
Tools
Zhao, Shuo, Ge, Yangyang, Ma, Liang, Yan, Tao, Lyu, Jingcai and Li, Zushu (2018) Formation analysis of edge cracks of 33MnCrTiB fork steel. Metals, 8 (8). 587. doi:10.3390/met8080587
|
PDF
WRAP-formation-analysis-edge-cracks-33MnCrTiB-fork-steel-Li-2018.pdf - Published Version - Requires a PDF viewer. Available under License Creative Commons Attribution 4.0. Download (5Mb) | Preview |
Official URL: https://doi.org/10.3390/met8080587
Abstract
A 33MnCrTiB is a high-strength low alloy steel used for a forklift truck. This study investigates the root causes of the edge cracks in 33MnCrTiB steel produced by a steel manufacturer. After sampling, inspecting and analyzing the 33MnCrTiB flat steel with edge cracks taken from the plant, it was found that the crack and porosity contain similar residues to the deoxidation products and continuous casting mold flux. It can be concluded that the edge surface cracking in the flat steel are mainly caused by the non-deformable inclusions in steel, slag sticking and surface cracks on the original billet. At the same time, the further expansion of cracks is closely related to the serious decarburization during the heating treatment in the billet heating process, and the improper rolling deformation system during the rolling process.
Item Type: | Journal Article | |||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Subjects: | T Technology > TN Mining engineering. Metallurgy | |||||||||||||||
Divisions: | Faculty of Science, Engineering and Medicine > Engineering > WMG (Formerly the Warwick Manufacturing Group) | |||||||||||||||
Library of Congress Subject Headings (LCSH): | Steel alloys -- Cracking, Forklift trucks, Porosity, Molding (Founding), Decarburization of steel, Steel -- Inclusions | |||||||||||||||
Journal or Publication Title: | Metals | |||||||||||||||
Publisher: | MDPI | |||||||||||||||
Official Date: | 27 July 2018 | |||||||||||||||
Dates: |
|
|||||||||||||||
Volume: | 8 | |||||||||||||||
Number: | 8 | |||||||||||||||
Article Number: | 587 | |||||||||||||||
DOI: | 10.3390/met8080587 | |||||||||||||||
Status: | Peer Reviewed | |||||||||||||||
Publication Status: | Published | |||||||||||||||
Access rights to Published version: | Open Access (Creative Commons) | |||||||||||||||
Date of first compliant deposit: | 1 August 2018 | |||||||||||||||
Date of first compliant Open Access: | 1 August 2018 | |||||||||||||||
RIOXX Funder/Project Grant: |
|
Request changes or add full text files to a record
Repository staff actions (login required)
View Item |
Downloads
Downloads per month over past year